Introduction JL-6130EVA transparent foam glue is designed for foam and plastic, foam, wood, metal, fabric and other materials bonding. Technical parameters consisting of single-component color transparent viscous liquid density (23 ± 1 ℃) about 0.98kg / l Viscosity (25 ± 0.5 ℃) 3000-6000 cps time 5-10min dry solids content of 40-50% Operating temperature -10 ℃ + 60 ℃ shelf life of six months (25 ℃) peel strength 7d / N / 25mm Foam - Foam: Tear products widely used in home appliances, printing, crafts, packaging, gifts and other industries. Product Features 1, single-component materials, easy to use operating room 2, excellent water resistance, a higher adhesion 3. Use a good transparency, surface treatment: The sticky surface cleaning treatment, guaranteed to be sticky surface dry No oil, no dust. 2, the optimum operating temperature is between 20 ℃ -30 ℃, should not be used at low temperatures and high humidity conditions. 3, when bonding nonporous material, after being sticky adhesive surface evenly, dry for 1-2 minutes, until slightly sticky when the bonding face of quasi joined together and compacted 1 to 2 hours, 48 hours after the optimum strength. 4, was sticky surface roughening treatment or secondary coating allows better bonding. 5, can be stored in a cool dry place. Notes 1, when using this product, the operating site must be well ventilated and operate in accordance with national regulations concerning the protection of labor. 2, this product is flammable chemicals, please stay away from children, fire, heat, temperature and shade airtight storage, is prohibited and oxidants, acids, alkalis mix chemicals, avoid prolonged exposure to uncured rubber skin. 3, the available amount of cyclohexane dilution, stir to use. 4, if accidentally splashed into the eyes, rinse immediately with plenty of water and seek treatment. [Storage] products to be ventilated, cool, dry place sealed. [Shelf Life] six months, expired after passing the test, you can continue to use the [packaging] 15 kg / drum 20 kg / plastic barrel